| Nozzle temperature | 200~240 ℃ |
|---|---|
| Bed temperature | 35~55 ℃ |
| Bed modification | PEI frosted board |
| Active cooling fan | ON, 50~100 % |
| Layer height | 0.2 mm |
| Shell thickness | ≥0.8 mm |
| Print speed | ≤400 mm/s |
| Material Properties | Typical Value | Test Method |
|---|---|---|
| Melt temperature | ~160℃ | ISO 11357 |
| Glass transition temperature | ~60℃ | ISO 11357 |
| Melt flow rate (MFR)1 | 2~5g/10min | ISO 1133 |
| Heat deflection temperature (HDT)2 | 60℃ | ISO 75 |
| Vicat softening temperature (VST)3 | 71℃ | ISO 306 |
| Density | 1.41–1.43g/cm³ | ISO 1183 |
| Odor | Odorless | / |
| Solubility | Insoluble in water | / |
1. Test conditions: T= 190℃; m= 2.16kg.
2. Test conditions: 0.45MPa; 120℃/h.
3. Test conditions: 10N; 120℃/h.